Consists of pure silver particles, binding agent and water. The binding agent is produced from natural pulp fibre.
During firing, the pure silver particles solidify, and turn into pure silver (over 99.96%) . The binding agent consists of carbon, hydrogen and oxygen, and when fired, results in the release of a small amount of carbon dioxide and steam during the firing process.
This product is a low temperature - firing clay that can be fired from 650℃, and turns into pure silver (over 99.96%) after firing. The special formula of this product allows for combining with glass, porcelain and ceramic materials, and is also suitable for firing with sterling silver finding or wire. (Use SV925 at the firing temperature 650℃, a hold time of 30 minutes is recommended).
The surface of the fired piece will be white and matte due to crystallization of silver during firing, but a fine silver finish can be obtained by polishing.
Kiln Fire: 650°C - 30 minutes Torch Fire: Red Glow for 5 minutes Shrinkage: 8-9%
Graphics and Colours should be used as a guide
Click anywhere on the page to refresh quantity pricing.