Includes three reusable nozzles S(0.41mm) M(0.84mm) L(1.19mm)
Apply fine details, fill cracks, close seams and attach findings to wet or dry clay. Use for drawing unique decorations, building up 3D design or filling in small gaps.
The consistency of clay in the Syringe is firmer than silver Paste and allows for more control and workability.
Consists of pure silver particles, binding agent and water. The binding agent is produced from natural pulp fibre.
During firing, the pure silver particles solidify, and turn into pure silver (over 99.96%) . The binding agent consists of carbon, hydrogen and oxygen, and when fired, results in the release of a small amount of carbon dioxide and steam during the firing process.
This product is a low temperature - firing clay that can be fired from 650℃, and turns into pure silver (over 99.96%) after firing. The special formula of this product allows for combining with glass, porcelain and ceramic materials, and is also suitable for firing with sterling silver finding or wire. (Use SV925 at the firing temperature 650℃, a hold time of 30 minutes is recommended).
The surface of the fired piece will be white and matte due to crystallization of silver during firing, but a fine silver finish can be obtained by polishing.
Kiln Fire: 650°C - 30 minutes
Torch Fire: Red Glow for 5 minutes
Shrinkage: 8-9%